0Cr19Ni9 TIG焊接接头的抗蚀性及电弧重熔 罗伟1 (1.浙江大学,杭州,310027) 摘要:研究了低碳奥氏体不锈钢0Cr19Ni9手工钨极氩弧焊(TIG)焊接接头表面抗蚀性能及电弧重熔对其抗蚀性能的影响.实验结果表明,受焊接热循环的作用,焊接接头热影响区的抗蚀性能,以及焊缝金属的抗蚀性能,较母材有所降低.但经微束等离子弧表面重熔后,由于接头表面重熔层的快速凝固作用,细化了重熔层组织,减小了显微偏析,抑制了碳铬化合物在晶界的沉淀析出,焊接接头的抗蚀性能得以显著提高. 关键词:0Cr19Ni9钢; 重熔; 焊接接头; 腐蚀; [全文内容正在添加中] ......
bonding was obtained between AZ91D and bare steel 0Cr19Ni9 where a gap existed at the interface; the metallurgical bonding was formed between AZ91D and Al-coated 0Cr19Ni9, which could be divided... of AZ91D/Al-coated 0Cr19Ni9 interface was higher than that of AZ91D/bare 0Cr19Ni9 interface, which confirmed that Al coating could improve the adhesive strength between AZ91D and 0Cr19Ni9 during liquid......
效率,能耗和阴极产物的影响.结果表明:在含Mn2+溶液浓度为30 g/L,(NH4)2SO4浓度为130 g/L,SeO2浓度为0.04g /L,初始pH值为7.0,电流密度为400 A/m2,电解温度为35 ℃时,铝阴极的阴极电流效率为85.8%,能耗为4870.9 kW·h/t,得到的金属锰纯度高于99.5%,晶型为α-Mn.与传统不锈钢阴极(0Cr19Ni9)对比,Mn2+在铝阴极表面的起始... steel (0Cr19Ni9), the onset potential of manganese electrodeposition on aluminum cathode is not changed, while the hydrogen evolution is suppressed at initial period of electrodeposition. Aluminum......
喷丸处理提高TP304H耐热钢锅炉管抗水蒸气氧化性能应用效果的观察 何家文1,李辛庚1 (1.西安交通大学材料科学与工程学院,西安,710049;2.山东电力研究院,济南,250002) 摘要:对TP304H(0Cr19Ni9)耐热不锈钢采用喷丸处理工艺进行表面处理,连同未处理管同时安装在1000t/h电站锅炉的屏式再热器上,实际运行7552 h后取样分析管子内壁高温水蒸气氧化情况.观察结果表明,喷丸处理减小了内氧化倾向,合金元素Cr在表层区域富集,氧化膜层的物相构成由Fe的氧化物转变为以Cr氧化物为主的形态,氧化膜更为致密,有效提高了耐热钢的抗水蒸汽氧化性能文中分析了喷丸对氧化机理的影响,并讨论了喷丸处理工艺对氧化过程中扩散机理的影响以及氧化膜物相组成的变化. 关键词:锅炉; 耐热钢; 喷丸; 水蒸气氧化; 腐蚀; TP304H; [全文内容正在添加中] ......
火电厂锅炉再热器管高温腐蚀研究 王学刚1,何家文2,李辛庚2,齐慧滨3 (1.山东电力研究院,山东,济南,250002;2.西安交通大学材料科学与工程学院,陕西,西安,710049;3.北京科技大学腐蚀与防护中心,北京市腐蚀,磨蚀与表面技术重点实验室,北京,100083) 摘要:对TP304H(0Cr19Ni9)钢锅炉再热器管内壁水蒸气氧化和外壁烟气高温腐蚀的锈层截面进行了观察与分析,确定了锈层的结构,成分和生长规律,并据此估算了管子的使用寿命.研究发现TP304H再热器管内壁在高温水蒸气环境下氧化产物层由外层和内层两部分组成,在外层与内层之间存在大量孔洞,并且外层发生了明显的剥落,剥落层厚度约为100μm.再热器管外壁则遭受含硫气氛的高温腐蚀和烟气冲刷磨损两种形式的破坏,烟气冲刷加剧了腐蚀的进行. 关键词:高温腐蚀; TP304H; 锅炉再热器管; 剩余寿命; [全文内容正......